抑制二氧化碳腐蚀的缓蚀剂及其缓蚀机理研究

doi:10.7623/syxb200405021

石油学报 ›› 2004, Vol. 25 ›› Issue (5): 104-107,112.DOI: 10.7623/syxb200405021

抑制二氧化碳腐蚀的缓蚀剂及其缓蚀机理研究

梅平¹, 艾俊哲², 陈武^1,2, 袁谷³

1. 长江大学化学与环境工程学院, 湖北荆州, 434023;
2. 华中科技大学材料科学与工程学院, 湖北武汉, 430074;
3. 北京大学化学与分子工程学院, 北京, 100871

收稿日期:2003-11-17 修回日期:2004-03-04 出版日期:2004-09-25 发布日期:2010-05-21
作者简介:梅平,男,1961年11月生,1982年毕业于华中师范大学,现为长江大学教授,主要从事应用电化学的教学与科研工作.E-mail:meipinghb@126.com.
基金资助:
国家863项目(863-820-07-01)"高温高密度测试液技术研究"和湖北省教育厅重点科研项目(2002A04011)"防止二氧化碳腐蚀的新型缓蚀剂研制及性能研究"部分成果.

Corrosion inhibitor resistant to carbon dioxide and its inhibiting mechanism

MEI Ping¹, AI Jun-zhe², CHEN Wu^1,2, YUAN Gu³

1. College of Chemical and Envionmental Engineering, Yangtze University, Jingzhou 434023, China;
2. College of Material Science and Engineering, Huazhong University of Science and Technology, Wuhan 430074, China;
3. College of Chemistry and Molecular Engineering, Peking University, Beijing 100871, China

Received:2003-11-17 Revised:2004-03-04 Online:2004-09-25 Published:2010-05-21

摘要/Abstract

摘要： 采用失重法、电化学极化曲线、X射线光电子能谱分析及扫描电镜,筛选出了能抑制二氧化碳腐蚀的缓蚀体系JS.研究了JS抑制二氧化碳腐蚀的电化学特征,分析了腐蚀前、后及加入缓蚀体系JS后N80钢的表面形貌及表面产物,探讨了JS的缓蚀机理.结果表明,由主剂JB和辅剂SM组成的复配缓蚀体系有良好的协同作用,产物膜有3层,能抑制二氧化碳对N80钢的腐蚀.

关键词: 二氧化碳腐蚀, 缓蚀剂, 缓蚀机理, 复配体系, 协同作用

Abstract: The corrosion inhibitor JS resistant to carbon dioxide corrosion was selected by means of weight-loss method,electrochemical polarization curve in the corrosion medium,X-ray photoelectron spectrometry and scanning electron microscope.The electrochemical property of JS resistant to carbon dioxide corrosion was investigated.The shape pattern and the products on the surface of N80 steel after corroded by carbon dioxide and adding JS inhibitor were analyzed.The inhibiting mechanism of JS inhibitor was researched.The experiment result shows that the compounded system of mayor inhibitor JB and the assistant inhibitor SM has good coordinate effects and corrosion resistance to carbon dioxide,because of three-layer products produced on the surface of N80 steel.

Key words: carbon dioxide corrosion, corrosion inhibitor, inhibiting mechanism, compounded system, coordination

中图分类号:

TE89

梅平, 艾俊哲, 陈武, 袁谷. 抑制二氧化碳腐蚀的缓蚀剂及其缓蚀机理研究[J]. 石油学报, 2004, 25(5): 104-107,112.

MEI Ping, AI Jun-zhe, CHEN Wu, YUAN Gu. Corrosion inhibitor resistant to carbon dioxide and its inhibiting mechanism[J]. Editorial office of ACTA PETROLEI SINICA, 2004, 25(5): 104-107,112.

[1]	王业飞, 杨震, 战风涛, 胡松青, 陈五花, 丁名臣. 喹啉季铵盐二聚体吲哚嗪衍生物的合成与酸化缓蚀性能[J]. 石油学报, 2019, 40(1): 67-73,114.
[2]	张智, 刘志伟, 谢玉洪, 李中, 李炎军, 张超, 韦龙贵, 段杰浩, 周琛洋. 井筒载荷-腐蚀耦合作用对碳钢套管服役寿命的影响[J]. 石油学报, 2017, 38(3): 342-347,362.
[3]	战风涛, 杨震, 吕志凤, 胡以朋, 潘原, 陈彦飞, 肖常林, 张婷. 高效缓蚀性氯化苄基喹啉衍生物制备与表征[J]. 石油学报, 2015, 36(9): 1116-1121.
[4]	林冠发, 白真权, 赵新伟, 郑茂盛, 路民旭. 温度对二氧化碳腐蚀产物膜形貌特征的影响[J]. 石油学报, 2004, 25(3): 101-105,109.
[5]	陆柱, 黄光团, 丛梅, 严文俊. 油田污水回注缓蚀剂的研制及机理[J]. 石油学报, 1995, 16(4): 161-166.
[6]	郑家燊, 赵景茂, 孙娈芬, 赵淑华. 高含硫钻井液缓蚀剂的合成及性能研究[J]. 石油学报, 1992, 13(1): 125-134.

抑制二氧化碳腐蚀的缓蚀剂及其缓蚀机理研究

Corrosion inhibitor resistant to carbon dioxide and its inhibiting mechanism

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 6

编辑推荐

Metrics

本文评价