Stress corrosion performance of N80 steel in formation water

doi:10.7623/syxb200602031

Editorial office of ACTA PETROLEI SINICA ›› 2006, Vol. 27 ›› Issue (2): 141-144.DOI: 10.7623/syxb200602031

• Petroleum Engineering • Previous Articles

Stress corrosion performance of N80 steel in formation water

Gu Chunyuan^1,2, Di Qinfeng¹, Wang Zhanghong²

1. Shanghai Institute of Applied Mathematics and Mechanics, Shanghai University, Shanghai 200072, China;
2. Sinopec Jiangsu Oilfield Company, Yangzhou 225009, China

Received:2005-05-24 Revised:2005-08-01 Online:2006-03-25 Published:2010-05-21

N80钢在地层水中的应力腐蚀行为研究

顾春元^1,2, 狄勤丰¹, 王掌洪²

1. 上海大学上海市应用数学和力学研究所, 上海, 200072;
2. 中国石化江苏油田分公司, 江苏扬州, 225009

作者简介:顾春元,男,1970年2月生,1993年毕业于西安石油学院,现为上海大学博士研究生,研究方向为油气田开发工程技术和工程力学.E-mail:wein1989@163.com
基金资助:
国家自然科学基金(50174047);上海市重点学科建设项目(Y0103)资助

Abstract

Abstract: The stress corrosion performance of N80 steel was experimented respectively under the condition of slow strain rate tension in air and formation water.The corroded fractures on the steel were analyzed with SEM.The fractures on columned samples of N80 steel showed lots of homogeneous dimples in air and was characterized by tough fractures.Many intercrystalline fractures appeared on the steel samples in formation water,which indicates the stress corrosion cracking sensitivity.The fracture shrinkage rates are not proportional to the extending rate,and the mechanical property of N80 steel is worse and influenced by strain rate and temperature.Under the action of stress,the corrosion rate of N80 steel samples increased 12 percent than that without stress.When some proper corrosion inhibitors are put into water,the stress corrosion decreasing rates was 38% to 43%,and the mechanical property can be improved.

Key words: N80 steel, stress corrosion, slow strain rate tension experiment, directional well, tough fracture, intercrystalline fracture

摘要： 分别在空气和地层水两种环境中进行了不同应变速率下N80钢的慢应变拉伸(SSRT)实验,并进行了断口电镜扫描分析.研究发现,N80钢在空气中断口为均匀的韧窝,呈韧性断裂;而在地层水中,出现了晶间断裂,显示出应力腐蚀断裂(SCC)的敏感性,力学性能明显降低,并受到应变速率与温度的共同影响.试片腐蚀率实验结果表明,在应力作用下的N80钢腐蚀速率比无应力状态下高12%,而添加适当的缓蚀剂可以减缓N80钢的应力腐蚀,缓蚀率为38%~43.2%,同时力学性能有所改善.

关键词: N80钢, 应力腐蚀, 慢应变拉伸实验, 定向井, 韧性断裂, 晶间断裂

CLC Number:

TE89

Gu Chunyuan, Di Qinfeng, Wang Zhanghong. Stress corrosion performance of N80 steel in formation water[J]. Editorial office of ACTA PETROLEI SINICA, 2006, 27(2): 141-144.

顾春元, 狄勤丰, 王掌洪. N80钢在地层水中的应力腐蚀行为研究[J]. 石油学报, 2006, 27(2): 141-144.

[1]	Zhang Zhi, Liu Zhiwei, Xie Yuhong, Li Zhong, Li Yanjun, Zhang Chao, Wei Longgui, Duan Jiehao, Zhou Chenyang. Influence of shaft load-corrosion coupling on the service life of carbon steel casing pipe [J]. Acta Petrolei Sinica, 2017, 38(3): 342-347,362.
[2]	Tian Jialin, Liu Gang, Yang Lin, Wu Chunming, Yang Zhi, Yuan Changfu, Fu Chuanhong, Li You. Characteristic of new-style PDC bit with whipstocking controllability [J]. Acta Petrolei Sinica, 2015, 36(7): 882-889.
[3]	Wu Chao, Zang Yanbin, Zhang Dongqing, Wu Jun, Chen Lin, Liu Chao. A method of borehole stability prediction while drilling directional wells and its application [J]. Acta Petrolei Sinica, 2015, 36(10): 1290-1298.
[4]	SHEN Yue ZHU Jun SU Yinao SHENG Limin LI Lin. Transmission characteristics of the drilling fluid pressure quadrature phase shift keying signal along a directional wellbore [J]. Editorial office of ACTA PETROLEI SINICA, 2011, 32(2): 340-345.
[5]	WANG Wenchang DI Qinfeng YAO Jianlin DOU Shengjun YOU Hongjuan. A new finite element method in analyzing mechanical properties of sucker rod strings in 3D directional wellbores [J]. Editorial office of ACTA PETROLEI SINICA, 2010, 31(6): 1018-1023.
[6]	Lü Xianghong, ZHAO Guoxian, ZHANG Jianbing, HAN Yong, CHANG Zeliang. Experimental study on corrosion behaviors of H₂S and CO₂ to 0.5 Cr steel used in gathering pipeline at simulated environment of Tarim Oilfield [J]. Editorial office of ACTA PETROLEI SINICA, 2009, 30(5): 782-787.
[7]	LIU Baixi1, LIU Hongzhao. Prediction of dynamic parameters of sucker-rod pumping system in directional well based on LuGre friction model [J]. Editorial office of ACTA PETROLEI SINICA, 2008, 29(6): 938-941.
[8]	LIU Leiming, ZHANG Faqiang, YAN Chengyu, YIN Jinyin, HUANG Xuebin. Study on a general mathematical model for suck and pumping system [J]. Editorial office of ACTA PETROLEI SINICA, 2008, 29(5): 769-772.
[9]	DONG Shimin, WANG Shengjie, LU Dongfeng, JI Shengzhu, HOU Weiqian, WANG Xitao. Simulation models for optimization design of suction parameters for rod pumping system in directional wells [J]. Editorial office of ACTA PETROLEI SINICA, 2008, 29(1): 120-123.
[10]	Jin Yan, Chen Mian, Zhang Xudong. Hydraulic fracturing initiation pressure models for directional wells in naturally fractured formation [J]. Editorial office of ACTA PETROLEI SINICA, 2006, 27(5): 124-126.
[11]	LU Gang, TONG Chang-hai, XING Yu-de. A model for design of three-dimensional multi-target wellbore trajectory based on restricted optimization [J]. Editorial office of ACTA PETROLEI SINICA, 2005, 26(6): 93-95.
[12]	LI Xing, WANG Feng, YU Guo. Research on progressing cavity pump lifting technique for shallow directional well [J]. Editorial office of ACTA PETROLEI SINICA, 2005, 26(3): 118-122.
[13]	LI Jun, CHEN Mian, ZHANG Hui. Study on varying rules of casing stress in directional hole with in-situ stress conditions [J]. Editorial office of ACTA PETROLEI SINICA, 2005, 26(1): 109-112.
[14]	TANG Xue-ping, SU Yi-nao, CHEN Zu-xi. Three-dimensional well-path planning model and its exact solution [J]. Editorial office of ACTA PETROLEI SINICA, 2003, 24(4): 90-93,98.
[15]	LIU Xiu-shan, PENG Guo-sheng, ZHAO Xiao-xiang. An advanced method for planning and surveying well trajectories of rotary steering drilling [J]. Editorial office of ACTA PETROLEI SINICA, 2003, 24(4): 81-85.

Stress corrosion performance of N80 steel in formation water

N80钢在地层水中的应力腐蚀行为研究

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 15

Recommended Articles

Metrics

Comments